PC(Polycarbonate) data sheet
--------------------------------------------------------------------------------
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P = poor
O = opaque - T = translucent- R = Rockwell - S = Shore
--------------------------------------------------------------------------------
STRUCTURE: Cr
SPECIFIC DENSITY: 1.2
WATER ABSORBTION RATE (%): 0.16
ELONGATION (%): 100
TENSILE STRENGTH (psi): 10000
COMPRESSION STRENGTH (psi): 12000
FLEXURAL STRENGTH (psi): 14000
FLEXURAL MODULUS (psi): 330000
IMPACT (IZOD ft. lbs/in): 2.4
HARDNESS: R75
FABRICATION
- BONDING: G
- ULTRASONIC WELDING: E
- MACHINING: E
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 287
- @ 264 psi: 270
UTILZATION TEMPERATURE (deg. F)
- min: -145
- max: 275
MELTING POINT (deg. F): 300
COEFFICIENT OF EXPANSION: 0.000039
ARC RESISTANCE: 11
DIELECTRIC STRENGTH (kV/mm): 15
TRANSPARENCY: C
UV RESISTANCE: G
CHEMICAL RESISTANCE
- ACIDS: G
- ALKALIS: P
- SOLVENTS: P
|